HDPE-g-MAH

It's produced by grafting high density polyethylene with maleic anhydride through reactive extrusion.

It's produced by grafting high density polyethylene with maleic anhydride through reactive extrusion. 

With the introduction of strong polar groups and the high grafting rate, this product has become the bridge between polar materials and non-polar ones.

Typical application of HDPE-g-MAH:

a)Used as interface modifier of glass fiber and mineral filled PE, greatly improve the compatibility of PE and the mineral filler, thereby considerably raise the mechanical properties like impact strength, tensile strength, flexural strength of the material.

b)Used in the alloy of PE and PA, it could significantly enhance the processibility and mechanical properties of the material, reduce the shrinkage rate, improve the dimensional stability of the final product.

c)Put in PE coating powder, significantly improve the coating and painting properties of PE.

Properties

Items	Specification	Typical value
Carrier resin	HDPE	HDPE
Appearance	White uniform particles	White uniform particles
Density(g/cm3)	0.94-0.98	0.946
MFI(2.16kg, 190°C)	2-4	3.21
Grafting rate	0.8-1.2	0.92
Tensile strength(Mpa)	>15	19.5
Elongation at break	>150	420
Melting point(°C)	>126	135

Packaging and storage:

Paper-plastic compound bag lined with PE film, 25kg/bag. Stored in dry, ventilated place.

HDPE-g-MAH